Development of direct fluorination technology for application to materials for lithium battery

Direct fluorination of 1,3-dioxolan-2-one with elemental fluorine was successfully carried out to provide 4-fluoro-1,3-dioxolan-2-one, which was expected as an additive for lithium ion secondary battery. 4-Fluoro-1,3-dioxolan-2-one was also further fluorinated with elemental fluorine to give three isomers of difluoro derivatives by the same methodology. Another topic is the preparation of trifluoromethanesulfonyl fluoride, an intermediate of lithium battery electrolyte, by the reaction of methanesulfonyl fluoride with elemental fluorine. The use of perfluoro-2-methylpentane as a solvent gave satisfactory selectivity of trifluoromethanesulfonyl fluoride.     

锂离子二次电池碳负极材料的改性

作为锂离子二次电池的碳负极材料，其改性方面的研究内容主要有：引入非金属元素，引入金属元素，处理表面及其它方面。纺入的非金属元素有硼，硅，氮，磷和硫。引入的金属元素有钾，铝，镓和钒，镍，钴，铜，铁等过渡金属元素。表面处理的方法包括氧化，形成表面层等。     

Fabrication of solid thin film electrolyte and LiCoO2 by aerosol flame pyrolysis deposition

Aerosol flame pyrolysis deposition method was applied to deposit the oxide glass electrolyte film and LiCoO₂ cathode for thin film type Li-ion secondary battery. The thicknesses of as-deposited porous LiCoO₂ and Li₂O–B₂O₃–P₂O₅ electrolyte film were about 6 μm and 15 μm, respectively. The deposited LiCoO₂ was sintered for 2 min at 700 °C to make partially densified cathode layer, and the deposited Li₂O–P₂O₅–B₂O₃ glass film completely densified by the sintering at 700 °C for 1 h. After solid state sintering process the thicknesses were reduced to approximately 4 μm and 6 μm, respectively. The cathode and electrolyte layers were deposited by continuous deposition process and integrated into a layer by co-sintering. It was demonstrated that Aerosol flame deposition is one of the good candidates for the fabrication of thin film battery.     

微波合成铝掺杂钻酸锂材料及性能研究

以LiOH·H2O，Al2O3和Co3O4为原料，微波加热合成Li离子电池正极材料LiAlxCo（1-x）O2．通过XRD测试表征了不同Al加入量时合成产物的晶体结构，确定当x≤0．4时，产物为单一相层状结构．计算了不同x时LiAlxCo（1-x）O2的晶胞参数，随着x的增大，a值减小，c值增大．对合成LiAlxCo（1-x）O2样品进行DSC—TGA测试，结果表明，当x不同时，合成样品的热稳定性不同．SEM测试表明，合成晶体粒度较均匀，粒径在5μm左右．电化学测试表明，LiAl0.2Co0.8O2的电化学性能最好，首次循环放电容量为127mAh／g，多次循环容量损失率小于LiCoO2．     

新型成膜电解液添加剂亚硫酸丁烯酯的电化学行为

合成制备了一种新的环状亚硫酸酯类有机溶剂——亚硫酸丁烯酯(BS). 量子化学计算结果表明, 亚硫酸丁烯酯有机溶剂分子的总能、LUMO值比碳酸丙烯酯有机溶剂的低, 具有较强的得电子能力, 不易被氧化. 其作为添加剂与碳酸丙烯酯(PC)混合应用于锂离子电池中, 可有效地抑制PC在石墨电极中的共插入, 能显著改善循环性能.     

Surface structure and electrochemical characteristics of natural graphite fluorinated by ClF3

Natural graphite samples with average particle sizes of 5, 10 and 15 μm (NG5 μm, NG10 μm and NG15 μm, respectively) were fluorinated by ClF₃ (3 × 10⁴ Pa) at 200 and 300 °C for 2 min. X-ray photoelectron spectra of surface-fluorinated samples showed that surface fluorine concentration increased with increase in the particle size of graphite and reaction temperature. Small amounts of chlorine were also detected in all the fluorinated samples. Raman spectra of original and surface-fluorinated samples indicated that the surface disordering was increased for NG10 μm and NG15 μm. Surface areas were decreased by the fluorination for NG5 μm and NG10 μm but unchanged for NG15 μm. The mesopores with diameter of 1.5-2 nm increased while those of 2-3 nm decreased for all the samples. First coulombic efficiencies for NG10 μm and NG15 μm were highly increased by surface fluorination in 1 mol/dm³ LiClO₄-EC/DEC/PC (EC: ethylene carbonate, DEC: diethyl carbonate, PC: propylene carbonate) solution.     

Synthesis and electrochemical properties of spinel LiMn2O4 prepared by the rheological phase method

Pure-phase and well-crystallized spinel LiMn₂O₄ powders were successfully synthesized by a simple rheological phase method. The thermal behavior and structure properties of the powders prepared by the rheological phase method compared with the solid-state reaction were investigated by thermogravimetry, powder X-ray diffraction , scanning electron microscopy and transmission electron microscopy. According to the results of the electrochemical tests, it is obvious that the sample resulting from the rheological phase method shows higher discharge capacity and better cycling stability than one formed in the solid-state reaction. The cyclic voltammogram and columbic efficiency curves also confirm that the product by the rheological phase method has a good cycling performance due to its fine cubic spinel structure and morphology.     

氯化钠对锂离子电池石墨负极的修饰改性

Numerous carbonaceous materials have been studied as anodes of lithium ion batteries during the past several years[1￣4].Graphite was favored for battery applications because it exhibits a high specific capac- ity, low working potential close to that of l…     

A DFT study of lithium battery materials: application to the β-VOXO4 systems (X=P, As, S)

VOXO₄ systems have been considered as potential lithium battery electrodes. They mainly present two distinct structural types: the tetragonal “α” type with a two-dimensional framework, and the three-dimensional orthorhombic “β”. DFT calculations were performed on this latter system for several β-Li_xVOXO₄ compounds (x=0, 1; X=P, As, S). They allowed to propose structural models for VOAsO₄ and LiVOSO₄, not fully crystallographically well described yet. Based on an experimental model of two-phase processes, these calculations led also to a good simulation of electrochemical potential values. A density of states analysis put in evidence the “inductive effect” and the role played by (XO₄)ⁿ⁻ groups inside the host frameworks on these potentials.     

PVC DISULFIDE AS CATHODE MATERIALS FOR SECONDARY LITHIUM BATTERIES

PVC disulfide (2SPVC) was synthesized by solution crosslink and its molecular structure was confirmed by infrared spectrum. 2SPVC's specific area is 36.1 m2·g-1 tested by stand BET method, and granularity experiment gives out the particle size of d0.5= 11.3μm. With SEM (Scanning Electron Microscope) experiment the surface morphology and particle shape of 2SPVC were observed. Cyclic voltammetry (scan rate: 0.5 mV·s-1) shows that 2SPVC experience an obvious S-S redox reaction in charge-discharge process. When 2SPVC was used as cathode material for secondary lithium battery in a 1 mol·L-1 solution of lithium bis(trifluoromethylsulfonyl) imide (Li(CF3SO2)2N) in a 5:45:50 volume ratio mixture of o-xylene (oxy), diglyme (DG) and dimethoxymethane (DME) at 30℃, the first discharge capacity of 2SPVC is about 400.3 mAh·g-1 which is very close to its theoretical value (410.5 mAh·g-1) at a constant discharge current of 15 mA·g-1. It can retain at about 346.1 mAh·g-1 of discharge capacity after 30 charge-discharge cycles. So 2SPVC is a very promising cathode candidate for rechargeable lithium batteries.